Kajian Transpor Zat (Ni Putu Sri Ayuni)

KAJIAN TRANSPOR ZAT WARNA AZO JENIS REMAZOL BLACK B
MENGGUNAKAN MEMBRAN KITOSAN

STUDY OF AZO DYE REMAZOL BLACK B THROUGH 
CHITOSAN MEMBRANE

Ni Putu Sri Ayuni1), I Nyoman Sukarta2), dan Komang Oktari Pradnyani3)
Jurusan Analis Kimia, Universitas Pendidikan Ganesha
Jalan Arjuna Singaraja-Bali
Email: 1)nps.ayuni@gmail.com; 2)sukartainyoman@gmail.com; 3)oktari_pradnyani@yahoo.co.id

Diterima Agustus 2014, diterima setelah perbaikan Januari 2015
Disetujui untuk diterbitkan Februari 2015

Abstrak: Penelitian tentang kajian transpor zat warna azo jenis Remazol Black B menggunakan membran kitosan telah dilakukan. Zat warna azo jenis Remazol Black B ditranspor menggunakan membran kitosan dengan variasi waktu kontak dan pH. Waktu kontak dan pH optimum, pola adsorpsi isotherm di analisis pada penelitian ini. Konsentrasi sisa larutan hasil transpor diukur menggunakan spektrofotometer UV-Vis. Dari pengukuran spektrofotometer UV-Vis diperoleh absorbansi dan konsentrasi. Untuk mengetahui karakteristik Remazol Black B oleh membran kitosan melalui uji isoterm Langmuir digunakan persamaan  dan isoterm adsorpsi Freundlich digunakan persamaan log(x/m) = log k+1/n log C, sedangkan daya adsorpsi maksimum dari adsorben ditentukan dari kurva berdasarkan karakteristik membran kitosan yang diperoleh. Membran kitosan berpotensi untuk transpor zat warna azo jenis Remazol Black B . Hasil transpor zat warna azo jenis Remazol Black B menggunakan membran kitosan diperoleh pada waktu kontak optimum 5 menit dan efisiensi transpor 92,88%, pH optimum 5 dan efisiensi transpor 92,17%. Transpor zat warna azo jenis Remazol Black B menggunakan membran kitosan mengikuti pola adsorpsi Langmuir (y=8406x–2698,4, R=0,992) dengan gradien 1/(x/m)maks=1,19 mg/g diperoleh daya adsorpsi maksimum 0,00119 g/g atau 1,19 mg/g. Transpor zat warna azo jenis Remazol Black B menggunakan membran kitosan tidak memenuhi pola adsorpsi Freundlich. 

Kata kunci: Remazol black B, kitosan, membran, dan transport.


Abstract: Research on transport studies azo dye Remazol Black B using chitosan membrane has been done. Azo dye Remazol Black B type was transported using chitosan membrane with variation of contact time and pH. The optimum of contact time, pH and pattern of adsorption isotherm were analyzed in this research. The concentration of residual transport resulting solution was measured using UV-Vis spectrophotometer. From the measurement of UV-Vis spectrophotometer absorbance and concentration was obtained. To determine the characteristics of Remazol Black B by chitosan membranes via Langmuir isotherm test used Freundlich adsorption isotherm equation  and use the equation log (x/m)=log k+1/n log C, while the maximum adsorption capacity of the adsorbent is determined from the curve based on the characteristics of chitosan membrane obtained. Chitosan membrane is potential for azo dye Remazol Black transport. The result shows that optimum transport of azo dye Remazol Black B using chitosan membrane were obtained at 5 min the efficiency of transport is 92.88%, pH 5 and the efficiency of transport is 92.17%. Langmuir adsorption pattern (y=8406x-2698.4) is suitable for azo Remazol Black B transport using chitosan membrane with a gradient of 1/(x/m) max=1.19 mg/g and maximum adsorption capacity 0.00119 g/g or 1.19 mg/g. Transport of azo dye Remazol Black B type using chitosan membrane does not fit the Freundlich adsorption pattern.

Keywords: Remazol black B, chitosan, membrane, and transport.